Inicio Boletín de la Sociedad Española de Cerámica y Vidrio Historical restorations of the Maqṣūrah glass mosaics from the Great Mosque o...
Información de la revista
Vol. 62. Núm. 3.
Páginas 204-219 (mayo - junio 2023)
Compartir
Compartir
Descargar PDF
Más opciones de artículo
Visitas
2044
Vol. 62. Núm. 3.
Páginas 204-219 (mayo - junio 2023)
Acceso a texto completo
Historical restorations of the Maqṣūrah glass mosaics from the Great Mosque of Córdoba
Las restauraciones históricas de los mosaicos de vidrio de la Maqṣūrah de la Gran Mezquita de Córdoba
Visitas
2044
Teresa Palomara,
Autor para correspondencia
t.palomar@csic.es

Corresponding author.
, Nadine Schibilleb, Luis Cerqueira Alvesc, Rafael Javier Díaz Hidalgod, María Auxiliadora Gomez-Moróne,f
a Institute of Ceramic and Glass, Consejo Superior de Investigaciones Científicas (ICV-CSIC), c/ Kelsen 5, Campus de Cantoblanco, 28049 Madrid, Spain
b IRAMAT-CEB, UMR5060, CNRS/Université d’Orléans, 3D, rue de la Férollerie, 45071 Orléans CEDEX 2, France
c C2TN, IST/CTN, University of Lisbon, E.N. 10, 2686-953 Sacavém, Portugal
d Department of Sciences of Antiquity and Middle Ages, Philosophy and Letters, University of Córdoba, Córdoba, Spain
e Andalusian Historical Heritage Institute (IAPH), Camino de los Descubrimientos s/n, 41092 Seville, Spain
f Department of Physical, Chemical and Natural Systems, University Pablo de Olavide, Ctra. de Utrera km. 1, 41013 Seville, Spain
Este artículo ha recibido
Información del artículo
Resumen
Texto completo
Bibliografía
Descargar PDF
Estadísticas
Figuras (17)
Mostrar másMostrar menos
Tablas (3)
Table 1. Description of non-mediaeval tesserae from the Great Mosque in Córdoba. Partially extracted from [17].
Table 2. Type of glass and LA-ICP-MS glass bulk composition (wt%), calculated as the average of three point analyses, in non-mediaeval tesserae from the Great Mosque in Córdoba. Partially extracted from [17].
Table 3. Summary of the main interventions and type of tesserae used in the Maqṣūrah of the Mosque-Cathedral of Córdoba.
Mostrar másMostrar menos
Abstract

The Great Mosque of Córdoba is the only mediaeval Islamic monument in al-Andalus that still contains some of its original 10th-century glass mosaic decoration, even though they were significantly altered and restored several times in the 18th, 19th and 20th centuries. By examining analytical, textual, and graphic evidence, this study attempts to reconstruct the different transformations of the Maqṣūrah, focusing on the glass mosaics in order to assess possible implications for their state of preservation. The results show that high-alkaline glass, which can be associated with modern tesserae, was used to restore the Miḥrāb and Sābāṭ mosaics. Modern pigments were also detected in the paints that were applied in situ to the surface of the colourless glasses. Textual and analytical evidences prove that Bāb Bayt al-Māl mosaic was completely removed in the 20th century and a replica with high-lead tesserae was installed in the same place.

Keywords:
Mosaic
Glass tesserae
Great Mosque of Córdoba
Historical restorations
Resumen

La Gran Mezquita de Córdoba es el único monumento islámico en al-Andalus que aún contiene restos de su decoración original del s. X en mosaico de vidrio, a pesar de haber sido significativamente alterada y restaurada en varias ocasiones en los ss. XVIII, XIX y XX. Mediante el estudio analítico y las evidencias gráficas y textuales, este estudio pretende reconstruir las diferentes transformaciones de la Maqṣūrah, especialmente en los mosaicos de vidrio para evaluar posibles implicaciones para su estado de conservación. Los resultados muestran que vidrios de alta alcalinidad, relacionados con teselas modernas, fueron utilizados para restaurar los mosaicos del Miḥrāb y el Sābāṭ. También se detectaron pigmentos modernos en las pinturas aplicadas in situ a la superficie de los vidrios incoloros. Las fuentes textuales y los estudios analíticos prueban que el mosaico del Bāb Bayt al-Māl fue retirado en el s. XX y una réplica con teselas ricas en plomo fue instalada en el mismo lugar.

Palabras clave:
Mosaico
Tesela de vidrio
Gran Mezquita de Córdoba
Restauraciones históricas
Texto completo
Introduction

Córdoba became the capital of the Roman province of Hispania Ulterior and was also an important administrative centre during the Visigoth period. The city prospered particularly after the Muslim conquest of the Iberian Peninsula, first as the capital of the Umayyad Emirate (756–929 AD), and later the Caliphate of Córdoba (929–1031 AD). ‘Abd al-Raḥmān I (Reign: 756–788 AD), the founder of the Umayyad dynasty of al-Andalus and the Emirate of Córdoba, commissioned substantial urban developments, including the construction of the Alcazar on the ruins of the Visigothic palace, and above all the foundation of the Great Umayyad Mosque (786–787 AD) [1–3]. The original Umayyad Mosque, finished by his son Hisham I, had eleven naves and twelve corridors from East to West (Fig. 1). This building was repeatedly modified and extended in the following centuries by ‘Abd al-Raḥmān II (∼840 AD), Al

akam II (∼960 AD), and Almanzor (988 AD) [4] (Fig. 1). In the process, the original qiblah was destroyed and a new Maqṣūrah, with three chambers, was built in the mid of 10th century (Fig. 1) [4–6]. The Miḥrāb in the centre is flanked by two lateral chambers, the Bāb Bayt al-Māl (treasury) on the left and the Sābāṭ chamber on the right connected with a corridor to the caliphal palace [7–9]. The façades of the three chambers (Bāb Bayt al-Māl, Miḥrāb, and Sābāṭ) and the dome of the entrance hall of the Miḥrāb were decorated with multicoloured glass mosaics mainly composed of gold leaf tesserae and different shades of red, green and blue (Fig. 2).

Fig. 1.

Plan of the Great Mosque of Córdoba indicating the different expansions and alterations.

(0.35MB).
Adapted from Biblioteca Digital Hispánica, Biblioteca Nacional de España [10].
Fig. 2.

Mosaics in situ: (a) the dome of the entrance hall of the Miḥrāb; (b) the Miḥrāb chamber; (c) Bāb Bayt al-Māl chamber; (d) Sābāṭ chamber.

(0.44MB).
Source: Authors.

The entrance hall of the Miḥrāb is crowned by a qubba almost 15m above floor level. It is divided by eight ribs into segments thus forming an octagon decorated with verses from the Quran [22:76; 22:77 & 22:78] along its eight sides [11]. The central cupola is divided into eight petals separated again by eight ribs (Fig. 2a). The façade of the Miḥrāb is decorated with a broad horseshoe arch formed of nineteen voussoirs with symmetric floral decorations on alternating red, gold, and blue backgrounds (Fig. 2b). Around the arch, a verse from the Quran [59:23] appears in a horizontal line with blue letters on a golden background. Around this verse and the arch appear two more verses [32:5 & 40:67] as well as an inscription that commemorates al

akam al-Mustanṣir as the patron of the mosaics. The inscription furthermore specifies that the work was carried out by the freeman and ḥäŷib (chamberlain) Ŷa’far ibn ‘Abd al-Raḥmān under the supervision of the ṣāḥib al-shurṭa (labour inspectors and police) Muḥammad ibn Tamlīj, Aḥmad ibn Naṣr, Jald ibn Hāšhim and Muṭarrif ibn ‘Abd al-Raḥmān from the kātib (secretary/scribe) [11,12]. These texts are written in vertical and horizontal lines, surrounding the arch. Seven niches on top of the arch are decorated with mosaics of flowers, symmetrically arranged.

The Sābāṭ and Bāb Bayt al-Māl façades, which are formed by an arch with 15 symmetric voussoirs, show the same mosaic consisting of vegetal motifs on red and gold backgrounds [4]. Around them, the alfiz was decorated with three texts alternating with geometric motives (Fig. 2c, d). The two inner inscriptions are commemorative texts about the work and the people involved in its execution, similar to the one from the Miḥrāb. However, the external inscription contains verses [2:236 & 3:6] from the Quran. The frames of the small windows above the mosaic are likewise decorated with Quranic verses [6:101 & 6:102] surrounded by the same geometric pattern. Under the horseshoe arch, verses [41:30, 41:31 & 41:32] are written in gold lettering on a blue background (Fig. 2c, d). Some inscriptions are partially lost. For example, the mosaic inscription on the façade of the Sābāṭ chamber was restored without following the original inscription.

The mosaics have undergone considerable changes over the centuries, especially in the aftermath of the building's conversion into a Christian cathedral in 1236 AD[4,8,13–16]. The original mosaics were thoroughly characterized in previous works [17,18] and, therefore, the main objective of the present study is to identify the historical changes and restorations of the Maqṣūrah mosaics based on a combination of textual and graphic sources as well as the material and compositional evidence of the mosaics. The close examination of the architectural and decorative modifications of the Maqṣūrah over time reveals the impact these had on the preservation of the mosaics. The characteristics of the different restoration campaigns in turn shed light on different traditions of conservation, which at different times were contingent on intrinsic cultural and aesthetic values and principles.

Methodology

For the historical review, different digital archives and libraries were consulted to obtain the historical documentation. This includes the Biblioteca Nacional de España, the Biblioteca Virtual de Prensa Histórica, the institutional repository of the Universitat Politècnica de Catalunya, and the Repositorio Real Academia de Córdoba, among others.

For the analytical characterization, 91 tesserae from the maqṣūrah mosaics of the Mosque-Cathedral of Córdoba were removed for analysis by optical microscopy (OM), scanning electron microscopy – energy dispersive X-ray spectroscopy (SEM-EDX), laser ablation inductively coupled plasma mass spectrometry (LA-ICP-MS), micro-particle-induced X-ray emission (μ-PIXE), Fibre Optic Reflectance Spectroscopy (FORS), and μ-Raman spectroscopy (for detailed description of the analytical methods see [17]).

Additionally to these techniques, Gas Chromatography (GC) was applied to identify the organic compounds of the paints. For the determination of lipophilic substances, such as drying oils, resins and waxes; and of hydrophilic substances, such as proteins and gums – polysaccharide (gum Arabic and related products), samples are treated with the Meth-prep II methylation reagent. For carbohydrates and proteins, a hydrolysis is carried out with microwave-assisted 6M HCl and a derivatization with MTBSTFA in pyridine of the resulting fatty acids, amino acids and monosaccharides.

Finally, Fourier transform infrared spectrometry (FTIR) was used to characterize the surface layers. The instrumental set-up was a PerkinElmer Spectrum 3 FT-IR/NIR Spectrometer coupled to an Attenuated Total Reflection (FTIR-ATR) accessory, microscopy spotlight 200 and detector MIR TGS. The analyses in cross-section were done with a spectral range from 4000 to 400cm−1 with a spectral resolution of 4cm−1.

Results and discussionMosaics’ creation and their modifications over the centuries

Muhammad al-Idrīsī, in the 12th century, and Ibn ‘I

ari, in the 14th century, wrote that the qiblah of the Great Mosque was decorated with al-fusayfisa al-mu
hab wa-l-mulwwan (golden and coloured mosaics) and muzŷŷaŷa (with glaze) tiles, which were sent by the emperor of Constantinople to ‘Abd al-Raḥmān III, father of Al
akam II [8,13,19]. The mosaics of the Miḥrāb and the dome, were the first to be finished, followed by the decoration of both lateral chambers [4]. An inscription on the Bāb Bayt al-Māl façade specifies that the decoration here was finished in 354H (965 AD). This date also appears in a marble inscription inside the Miḥrāb and in the cymatium of the Miḥrāb’ arch [11,20]. Ocaña Jiménez argues that since the date appears in a restored part of the mosaic it may have been incorrectly attributed, and that a date in late 360H (971 AD) is more likely for the completion of the mosaics [11]. The mosaics of the Sābāṭ door appear to have been finished between 970 AD and 973 AD[21]. The left border of the mosaic of the Sābāṭ door was mutilated around the year 366H (976 AD) in connection with the opening of a narrow door to the left, where the Minbar (wooden pulpit) was typically stored [4].

On 29 June 1236, King Ferdinand III of Castile conquered Córdoba and the Bishop of Osma (Soria) consecrated the Great Mosque of Córdoba as a Christian church, dedicated to the Assumption of the Virgin. It eventually became the Cathedral of Córdoba and in 1368–1371, King Henry II of Castile ordered substantial architectural modifications to turn the mosque into a proper Christian ecclesiastical structure (Fig. 1) [1,22–25]. In this process, the Miḥrāb was converted to the sacristy of the chapel of Saint Peter known as the Chapel of Zancarrón (Fig. 3).

Fig. 3.

Plans of the Great Mosque of Córdoba (a) original, and (b) around 1804. Legend: 1. Main place to keep the Quran or Book of the Law; 2. Pulpit where the Mufti, or high Priest, explained the Law; 3. Rooms of the priests and servants of the Mosque; 4. Place accessed only by priests and people dedicated to worship. 16. Chapel of Saint Bartholomew; 17. Chapel of Saint Philip and Santiago; 18. Chapel of Saint Peter, commonly known as Zancarrón; 19. Chapel of the Last Supper; 20. Chapel of Cardinal Salazar, currently Main Sacristy.

(0.28MB).
Source: Biblioteca Digital Hispánica, Biblioteca Nacional de España [10].

From documentary and pictorial evidence we know that in 1390, the mosaics of the Miḥrāb were partially covered up with an altarpiece depicting Saint Catherine of Alexandria, Saint Francis of Assisi, Saint Peter, Saint Paul, and the Nursing Madonna [26–28]. The chapel progressively fell into total disrepair and was all but forgotten. In 1892, a newspaper notice in the Diario de Córdoba pointed out the existence of a partition wall in front of the Miḥrāb[27]. This agrees with the existence of a wall in front of the door and a corridor on the right side of the Sābāṭ chamber that appears in the historical plans of the Mosque made in the 18th century by the architects Juan de Villanueva and Juan Pedro Arnal (Fig. 3b) [10,29–31] and in an engraving from 1812 [32,33]. This wall was also hinted at in the description of the chapel of Saint Peter by Ambrosio de Morales in 1572 [34]. The historian described the chapel as consisting of two rooms (one inside the other) decorated with mosaics and another small room (inside the inner one), the Miḥrāb[34]. He described the decoration as a delicate mosaic work with small patterns of floral motifs and pointed out that the designs were less perceptible in the mosaic of the lateral chamber than in the Miḥrāb façade, probably due to low contrast, reduced lighting or poor conditions of the mosaic.

Until 1586, the Bāb Bayt al-Māl chamber to the left of the Miḥrāb housed the sanctuary of the cathedral [35]. In 1595, the canons Antonio and Hernando Mohedano de Saavedra founded the Chapel of the Last Supper in the Bāb Bayt al-Māl and covered the mosaics with the canvas of the “La Última Cena” (“Last Supper”) by Pablo de Céspedes [35–37]. The canvas, which is still in the building, completely covered the façade of the chamber, as a result of which the mosaics fell into oblivion. Ancient plans of the mosque show a wall behind the canvas both in the theoretical mosque as well as in drawings of the cathedral (Fig. 2) [10]. Some engravings and photographs from the 19th century show the canvas in its original location in front of the mosaic [28,38–40] (Fig. 4). Even newspaper reports and books denied the possibility of the existence of two lateral chapels to either side of the Miḥrāb[23,41,42]. It was believed that they had disappeared entirely during the 15th-century modifications initiated by the bishop Iñigo Manrique [43].

Fig. 4.

Lithograph of the Maqṣūrah in 1879 with the altarpiece in front of the Bāb Bayt al-Māl.

(0.16MB).
Source: UPCommons [28].

For more than two centuries, the mosaics were covered with altarpieces. As a consequence of the Lisbon earthquake in 1755, several parts of the Mosque-Cathedral were severely damaged, such as the tower, causing serious structural damages [14,44]. The Miḥrāb dome was probably also affected because in 1767, the cathedral chapter ordered its repair as water filtered through several leaks into the chapel that increasingly sank into total ruin [45,46]. The repairs were carried out in 1771 under the direction of the French architect Baltasar Dreveton and cost 24,000 reals [45,47]. According to the orders of the dean, the restorations were made “without altering or changing anything of the architecture” [14,15,45,46] following the principles of the San Fernando Royal Academy of Fine Arts [48,49]. There is no information about the restoration materials, but Romero de Torres pointed out that the horseshoe arches from the latticework, which act as skylights, were painted [13,14].

In 1815, Pedro Antonio de Trevilla, bishop of Córdoba, ordered the dismounting of the altarpiece of the Nursing Madonna and other furniture that was kept in the Chapel of Saint Peter. This led to the re-discovery of the mosaics of the Miḥrāb and the Sābāṭ, which were heavily damaged, especially in the lower part of the mosaics as a consequence of the installation and removal of the altarpieces [50]. Patricio Furriel was hired by Tiburcio María de la Torre, acting Governor of Córdoba, to restore the mosaics in 1817–1818 [47]. According to the documentary evidence, work was carried out on the lower part of the voussoirs and the intrados of the Miḥrāb as well as the lower part, frame, and part of the inscriptions of the Sābāṭ mosaic. In areas where the tesserae were lost, the mortar was painted and colourless glasses were fixed with screws or glue, so the colour was visible [8,42,47]. These parts are easily identifiable to this day (Fig. 5). Some of the material we analyzed appears to confirm this remark (see Section 3.2). Stern suggested that Patricio Furriel also used patê de verretesserae in some areas such as the pendentives, the ribs of the dome, some parts of the window frames and in the central voussoirs of the Sābāṭ façade[13]; however, he might have confused them with lead glass tesserae, which appear very homogenous [17]. In places where the motifs were completely destroyed, Furriel re-designed the decoration in a baroque style, introducing some modifications in the epigraphic texts [8,43,47]. As a result of this intervention, eleven of the nineteen voussoirs of the Miḥrāb arch were restored, leaving only the central eight voussoirs in their original state. Similar interventions were carried out on the façade of the Sābāṭ chamber, where only the 5th to the 11th voussoirs still have their original decoration (Fig. 6).

Fig. 5.

Different interventions in the mosaics: (a) painted mortar, (b) painted mortar with restoration tesserae, (c) painted mortar and modern tesserae on a plaque fixed with screws. The exact location of these interventions is shown in Fig. 6.

(0.67MB).
Source: Authors.
Fig. 6.

Schematic representation of the different interventions on the basis of textual and graphic material, highlighting the areas from where the photos were taken for Fig. 5.

(0.32MB).
Images adapted from G. Ruiz Cabrero, G. Rebollo, and S. Herrero's planimetry.

In 1912, the canvas of “La Última Cena” was removed, revealing the mosaics of the Bāb Bayt al-Māl façade. The construction of the adjacent chapel of Cardinal Salazar (Fig. 3) together with the mounting and dismounting of the altarpiece resulted in the destruction of the mosaic [16]. For this reason, the Cathedral Chapter of Córdoba ordered their complete restoration. In keeping with the principles of Eugène Viollet-le-Duc, the architect responsible for the restoration campaign, R. Velázquez Bosco, commissioned a replica of the mosaic from the atelier J. & H. Maumejean Fréres in Madrid. A. Gilbert, the artistic director of the atelier, hired the Venetian mosaic artist F. Morolin to make the facsimile that was installed in 1916 [4,13,16,51,52] (Fig. 6).

Finally, in 1997 and 1999, the dome was consolidated by the Andalusian Historical Heritage Institute (IAPH) due to the poor condition of the mortars that contributed to the dislodging of the tesserae. This pathology was directly related to water infiltration. The fallen tesserae were reintegrated in the mosaics [53].

Characterization of the restoration's tesserae

The analyses of 91 tesserae revealed highly variable compositions (Fig. 7). Of the ten compositional groups, eight groups can be attributed to the original tenth-century decoration, including three types of Byzantine high boron glasses (number of tesserae, n=46), two different types of soda-rich plant ash glasses (n=9), and two types of high lead glasses (n=14) as well as a single sample that represents the re-use of a Roman tessera (MAQ C 042) [17,54]. The remaining 21 tesserae can be attributed to non-mediaeval material from later restorations due to the morphological characteristics and chemical composition of the glasses (Table 1). A principal component analysis (PCA) was performed on a selected subset of LA-ICP-MS data (Cs, Sr/CaO, Al2O3, Cl, PbO, As, Sb) using the openly accessible RESET database (https://c14.arch.ox.ac.uk). These elements were chosen as they represent the mineral impurities in the silica source (e.g. Al2O3), the alkali and alkaline earths (Cs, Sr/CaO), chlorine that can separate ancient from modern raw materials [55,56], the type of glassy matrix (PbO) as well as additives (As, Sb) that have a clear chronological range. The first two principal components (PC) cover 68% of the variance of the dataset and single out the 20th-century tesserae as having elevated As, Sb, and very low alumina, chlorine and strontium to lime ratios (Fig. 7; Table 2). These features indicate the use of modern raw materials, and the elevated arsenic and antimony levels clearly point to a date after the 17th-century date [57]. Seven painted tesserae (MAQ O 004, MAQ O 005, MAQ O 007, MAQ O 030, MAQ C 001, MAQ C 014, MAQ C 037) (Table 1) were also identified as material originating from restoration campaigns but with very different compositional characteristics [17].

Fig. 7.

Principal Component Analysis (PCA) of the 91 analyzed tesserae divided according to the different groups of compositions [17]. Please note that the coefficient vectors are given on an enlarged scale (2×).

(0.13MB).
Table 1.

Description of non-mediaeval tesserae from the Great Mosque in Córdoba. Partially extracted from [17].

Location  Name  Colour  Core description  Chromophore  Crystalline inclusions  Surface painted 
Bāb Bayt al-Māl door  MAQ E 001base  Yellowish  Transparent  Fe2+     
  MAQ E 001cart  Yellowish  Transparent       
  MAQ E 002  Red  Opaque  Cu0, Cu2+     
  MAQ E 003  Blue  Small crystals (white and red)  Co2+  KAlSi3O8, Pb2Sb2O7, Ca2Sb2O7   
  MAQ E 004  Blue  Small crystals (white and red)  Co2+  KalSi3O8, Pb2Sb2O7, Ca2Sb2O7   
  MAQ E 005  White  Small white crystals  Fe3+Pb2Sb2O7, Ca2Sb2O7   
  MAQ E 006  Red  Opaque  Cu0     
  MAQ E 007  Black  Small crystals (white and red)  Co2+  Pb2Sb2O7, Ca2Sb2O7   
  MAQ E 008  Dark grey  Small crystals (white and red)  Co2+, Fe3+  Pb2Sb2O7, Ca2Sb2O7, SiO2   
  MAQ E 009  Red  Opaque  Cu0  Pb2Sb2O7   
  MAQ E 012  Black  Small crystals (white and red)  Co2+, Fe3+, Cu2+0,0 Mn3+Pb2Sb2O7, Ca2Sb2O7, SiO2, Fe2O3   
  MAQ E 013  Light grey  Small white crystals  Cu2+  Pb2Sb2O7, Ca2Sb2O7   
  MAQ E 014  Light blue  Small crystals (white and red)  Co2+, Cu2+  KalSi3O8, Pb2Sb2O7   
  MAQ E 015  Light grey  Small white crystals  Co2+, Cu2+  Pb2Sb2O7, Ca2Sb2O7   
Sābāṭ door  MAQ O 004  Burgundy  Transparent     
  MAQ O 005  White  Homogeneous opaque matrix    Ca2Sb2O7 
  MAQ O 007  Burgundy  Transparent     
  MAQ O 030  Light blue  Transparent, homogeneous  Cu2+   
Miḥrāb door  MAQ C 001  Colourless  Transparent     
  MAQ C 014  Colourless  Transparent     
Miḥrāb ceiling  MAQ C 037base  Burgundy  Transparent       
  MAQ C 037cart  Burgundy  Transparent       
  MAQ C 042  Dark blue  Isolated small crystals       
Table 2.

Type of glass and LA-ICP-MS glass bulk composition (wt%), calculated as the average of three point analyses, in non-mediaeval tesserae from the Great Mosque in Córdoba. Partially extracted from [17].

Location  Name  Composition  (wt%)ppm
      Na2MgO  Al2O3  SiO2  P2O5  Cl  K2CaO  TiO2  MnO  Fe2O3  CuO  SnO2  PbO  As  Sr  Sb 
Bāb Bayt al-Māl door  MAQ E 001 base  Lead-silica glass  17.1  0.13  0.20  53.1  0.04  0.13  1.92  2.07  0.02  2.78  3.73  0.02  0.011  18.4  502  50  535 
  MAQ E 001 cart  Lead-silica glass  15.8  0.11  0.24  59.6  0.04  0.13  4.36  2.19  0.03  2.53  0.75  0.04  0.037  13.7  510  35  1963 
  MAQ E 002  Lead-silica glass  14.8  0.20  0.82  58.6  0.04  0.16  1.45  4.71  0.03  0.40  2.24  2.83  0.067  13.0  744  71  2493 
  MAQ E 003  Lead-silica glass  17.8  0.19  0.44  59.9  0.02  0.18  0.64  5.59  0.02  0.40  0.65  0.51  0.036  12.0  475  70  10,401 
  MAQ E 004  Lead-silica glass  15.2  0.20  0.57  56.2  0.02  0.26  0.80  4.88  0.03  0.21  0.38  1.12  0.022  17.6  511  41  19,786 
  MAQ E 005  Lead-silica glass  15.6  0.14  0.56  57.7  0.01  0.18  0.73  6.04  0.02  0.08  0.21  0.16  0.005  15.6  138  96  22,717 
  MAQ E 006  Lead-silica glass  16.3  0.76  1.17  61.1  0.21  0.66  1.94  5.97  0.06  0.29  3.33  1.86  0.112  5.85  330  428  1291 
  MAQ E 007  Lead-silica glass  14.5  0.25  0.69  56.3  0.04  0.14  0.67  5.41  0.04  2.64  0.94  0.37  0.036  15.9  577  139  12,530 
  MAQ E 008  Lead-silica glass  20.3  0.15  0.35  62.5  0.01  0.16  0.18  6.28  0.02  0.03  0.26  0.16  0.012  8.94  112  78  4021 
  MAQ E 009  Lead-silica glass  16.3  0.62  1.21  59.3  0.15  0.37  1.48  5.99  0.06  0.39  3.21  1.82  0.148  8.37  486  304  1868 
  MAQ E 012  Lead-silica glass  14.4  0.37  0.49  57.4  0.08  0.23  2.07  5.33  0.03  2.51  0.80  0.68  0.099  14.4  1006  118  5800 
  MAQ E 013  Lead-silica glass  8.8  0.18  0.35  48.9  0.02  0.16  0.59  5.22  0.02  0.17  0.25  0.94  0.073  31.9  472  71  19,374 
  MAQ E 014  Lead-silica glass  17.9  0.19  0.42  59.9  0.02  0.17  0.63  5.62  0.02  0.40  0.63  0.52  0.035  12.0  481  72  10,814 
  MAQ E 015  Lead-silica glass  16.2  0.31  0.61  55.8  0.03  0.19  1.07  5.41  0.03  0.59  0.56  1.40  0.095  15.2  1238  69  17,920 
Sābāṭ door  MAQ O 004  High-lime-low-alkali glass  8.6  0.78  0.85  70.1  0.19  0.75  4.25  14.0  0.12  0.021  0.30  0.002  2E-04  0.003  159   
  MAQ O 005  Mixed-alkali glass  7.7  2.92  1.09  61.3  0.19  0.61  9.45  8.55  0.15  0.025  0.48  0.010  7E-04  1.241  6533  491  44,026 
  MAQ O 007  Soda-rich glass  10.4  0.76  0.62  72.3  0.39  1.03  1.20  12.9  0.15  0.009  0.23  0.001  2E-04  0.001  150 
  MAQ O 030  Soda-rich glass  10.2  0.80  0.88  71.7  0.22  1.01  0.93  13.7  0.17  0.010  0.31  0.000  1E-04  0.003  207   
Miḥrāb door  MAQ C 001  Calco-potassic glass  2.6  0.27  0.27  68.9  0.19  0.23  18.7  8.61  0.03  0.008  0.11  0.003  4E-05  0.000  558  42   
  MAQ C 014  High-lime-low-alkali glass  9.6  0.52  2.92  68.3  0.35  0.74  4.15  12.8  0.06  0.021  0.40  0.001  2E-04  0.001  207   
Miḥrāb ceiling  MAQ C 037 base  Soda-rich glass  19.9  0.19  0.48  74.4  0.08  1.59  0.15  2.77  0.03  0.004  0.19  0.000  3E-05  0.000  54  17   
  MAQ C 037 cart  Soda-rich glass  19.7  0.20  0.46  74.5  0.08  1.60  0.15  2.82  0.03  0.004  0.18  0.000  3E-05  0.000  52  17   
  MAQ C 042  Soda-lime silicate glass  16.8  1.00  1.99  68.0  0.08  0.87  0.52  6.55  0.07  0.21  0.93  0.25  0.004  0.34  112  392  18,348 
Painted samples

Most of the seven painted restoration tesserae were transparent, colourless or weakly coloured glasses (Table 1). It was not possible to characterize the chromophore by FORS because its pale hue reduced the light reflected from the surface. Their analysis showed a great variety of compositions (Table 2) such as soda-rich glasses (MAQ C 037, MAQ O 007, and MAQ O 030), a calco-potassic glass (MAQ C 001), a mixed-alkali glass (MAQ O 005), and high-lime-low-alkali glasses (MAQ C 014 and MAQ O 004).

The soda-rich glasses have a chemical composition similar to some 17th-century glasses, specifically European Façon de Venise, Venetian common, or Vitrum Blanchum[58]. This composition has been maintained in commercial glasses from the second half of the 19th century and the first decades of the 20th century [59,60]. The potash glass was similar to that developed in Central Europe in the 17–19th century [59,61]. The white glass MAQ O 005, found in one voussoir of the Sābāṭ door, has similar amounts of Na2O and K2O (7% and 9.5%, respectively) and it was classified as mixed-alkali glass. Even though its content did not agree with 17th-century mixed-alkali glasses [58], the combination of a very homogeneous matrix opacified by Ca2Sb2O7 crystals and high arsenic levels indicates a post-17th-century date [62,63].

Despite their different composition, the painted tesserae located in the Sābāṭ door (MAQ O 30, MAQ O 05, MAQ O 07, and MAQ O 04) have high levels of TiO2 relative to Al2O3 as a common feature (Table 2). This provides solid evidence that these glasses are derived from different raw material sources and represent a distinct production from the other samples in the Miḥrāb mosaics, especially with respect to the silica source.

The surface of these tesserae together with 11 original tesserae[17] was coated with different colours (blue, red, green, and golden) (Fig. 8). The analyses made by SEM-EDX and PIXE detected high contents of lead in the surface paints (Fig. 9), and FTIR-ATR confirmed the use of white lead (2PbCO3·Pb(OH)2) (Fig. 10a), as a base where pigments were dispersed. High contents of iron and alumina was detected in green crystals of the green paints (Figs. 8a and 9a) that could be related to the use of iron aluminosilicates. In the blue paints, FTIR-ATR spectra identified the Prussian blue – Fe4[Fe(CN)6]3 – as pigment (Figs. 8b and 10a), while the high levels of mercury detected by SEM-EDS in the red paint agrees with the use of vermilion – HgS – (Fig. 8c) to produce the red paint. Grains of hematite – Fe2O3 – (45.6 – 216μm) were also detected on the red paint, as well as calcite grains on the blue. To restore the golden areas, the surface was covered with a preparative layer to which the gold leaf was applied, occasionally even over an original gold-leaf tessera (Figs. 8d and 9b). A yellowish adhesive, identified by FTIR-ATR as gum tragacanth, was identified on some reposition tesserae (Fig. 8e).

Fig. 8.

OM image (a–c) different paint layers on glass tesserae; (d) gold-plating on an original gold-leaf tessera, (e) tessera with adhesive.

(0.37MB).
Fig. 9.

PIXE maps (a) original tessera painted with white lead and green aluminosilicates (MAQ O 03), (b) original gold-leaf tessera with a preparation layer and a second gold leaf (MAQ C 34), (c) modern painted tessera (MAQ O 05).

(1.96MB).
Fig. 10.

FTIR-ATR spectra of (a) the blue paint on the tessera MAQ O 30, (b) the adhesive on the tessera MAQ O 13. Peaks attributions made using [64,65].

(0.22MB).

Vermilion as red and lead white as white pigments were known since ancient times [66,67]; Prussian blue, however, was introduced only in the early 1700s, being widely used until 1970 when it was replaced by the phthalocyanine blue [68]. The glasses are similar to those of the 17th and 18th centuries. They may have either been imported to the Iberian Peninsula or produced by Italian or Bohemian glass makers in Spanish factories [69].

The analyses of the green painting layer on the Byzantine sample MAQ C 025 by GC showed the presence of linseed oil and traces of conifer resin as binders of the paint without residue of varnish, and FTIR-ATR identified gum tragacanth in sample MAQ O 13. The use of linseed oil together with white lead was already used in antiquity and described by Heraclius for the preparation layers on a wooden support [70]. It was particularly popular during the Renaissance until the middle of the 20th century when it was replaced by cobalt or zirconium-based driers due to toxicological and environmental concerns [71].

It is thus reasonable to conclude that all the painted tesserae are related to the intervention of 1817–1818. The fact that both original and new samples were painted suggests the paint was applied directly to the mosaic surface in some areas. The implicit goal of the 19th-century restoration was to restore the Islamic mosaics without altering their overall appearance. The original parts were not touched but the gaps were filled with painted glass and plaques of modern tesserae. This approach is similar to the modern tradition of conservation, which consists of preserving the original areas as much as possible and filling in the missing parts with materials that are easily recognizable, while preserving the overall appearance of the work from a distance [72].

The 20th-century tesserae

The other group of non-mediaeval tesserae (n=15) was formed by the samples from the Bāb Bayt al-Māl door, and includes one transparent gold-leaf tessera, red opaque samples, and coloured bulk glasses with a high density of crystals (Table 1). All of them were lead-silica glasses with high contents of Na2O (17–20wt%) (Table 2). In comparison with the historical tesserae, they have higher contents of arsenic, antimony, and low levels of aluminium oxide and chlorine (Fig. 7) [17].

The gold-leaf tessera was formed by a transparent glass support with a leaf of gold (∼16μm of thickness) on its surface that was protected by a thin layer of glass, the so-called cartellina (∼500μm). The composition of the cartellina was slightly different from the support [17].

The red tesserae were completely opaque due to the presence of small nanoparticles of copper (Fig. 11a), which agrees with the high content of copper and iron in these samples (Table 2). The red glasses do not contain additional inclusions; however, isolated crystals of Pb2Sb2O7 were detected in one of the analyzed samples (MAQ E 009).

Fig. 11.

FORS spectra of the tesserae (a) MAQ E 002, (b) MAQ E 004 and (c) MAQ E 012. Bands attributions made using [73].

(0.34MB).

The transparent glasses with inclusions (Fig. 11) have a similar composition despite a great variety of colours due to the addition of chromophores. Co2+ and Cu2+ ions are the most common chromophores in the bluish and greyish tesserae (Fig. 11b) (Table 1). The black samples also contain manganese to darken the glass colour (Table 2), but the absorption bands were difficult to be distinguished due to the overlapping of the bands from the different chromophores (Fig. 11c).

Lead antimonate (Pb2Sb2O7) and calcium antimonate (Ca2Sb2O7) particles dispersed the light in most of the tesserae, independent of their colouration (Table 1). Pb2Sb2O7 inclusions are small yellowish crystals (∼20μm), and Ca2Sb2O7 accumulate into very small deposits forming large and irregular structures (150–250μm). Some regular feldspars (KAlSi3O8) were additionally detected in the blue tesserae (Fig. 12a), but typically in smaller amounts than the antimonate crystals. An agglomeration of SiO2 and Fe2O3 in varying proportions was found in the black samples (Fig. 12b) that may be residues of the sand raw material. Similarly, the dark grey sample displayed some big rounded quartz grains (∼300μm). In all cases, the addition of these big inclusions modified the material and optical properties and contribute in case of the mosaic tesserae to an increase in glass opacity.

Fig. 12.

OM and μ-Raman spectra of inclusions in tesserae (a) MAQ E 003 and (b) MAQ E 012. Legend: CA: Calcium Antimonate, Ca2Sb2O7; F: Feldspar, KAlSi3O8; P: Bindheimite, Pb2Sb2O7; H: Hematite, Fe2O3; Q: Quartz, SiO2; B: Alkaline sulphate. Attributions made using the RRUFF database on minerals and [74–76].

(0.48MB).

Tesserae with similar features (high-lead silicate glasses with lead and calcium antimonate) were found in the 18th-century tesserae from the Capela de São João Baptista (Lisbon, Portugal) [77]; although each colour showed different compositions with concentrations of PbO from 2wt% to ∼50wt%. These evidently modern tesserae appeared only in the mosaic from the Bāb Bayt al-Māl door and not in the other two façades. This means that the other mosaics in the Great Mosque were probably not touched during the early 20th-century restorations. This agrees with the news published at the beginning of the 20th century that talked about the installation of a mosaic facsimile due to the poor state of conservation of the original one following the principles of “stylistic restoration” by Eugène Viollet-le-Duc [78,79].

Conclusions

The mosaics of the Mosque-Cathedral of Córdoba offer a unique opportunity to study the evolution of the architectural and decorative traditions and the significance attributed to them over the centuries because the various restoration campaigns reflect changing attitudes towards the cultural and aesthetic value of Islamic art and architecture, as well as a paradigm shift in art conservation.

In the first centuries, the mosaics were part of the private Maqṣūrah of the caliph. Access was only allowed to people dedicated to worship and religious service. This testifies to the value and prestige associated with the art of glass mosaics. After the Christian conquest, the Islamic mosaics were covered with altarpieces, either because the mosaics were deemed inappropriate in the context of the ecclesiastical space of the cathedral or mosaics were no longer considered a desirable art form. The main degradation factor of the mosaics was the water leaks and dampness in the walls, which caused the mortar to disintegrate and the glass tesserae to detach. The lack of ventilation, especially during the period when the mosaics were hidden, together with the mounting and dismounting of the altarpieces accelerated this process, so that the lower parts of the Miḥrāb and Sābāṭ mosaics and the whole of the Bāb Bayt al-Māl mosaics were lost entirely.

The façades of the Miḥrāb and the Sābāṭ still preserved original mosaic tesserae, despite different interventions particularly in the 19th and 20th centuries. In the first quarter of the 19th century, colourless tesserae were inserted and painted to reproduce the colour of the original mosaics. The high-alkaline silicate composition of these glasses identifies these tesserae as modern glass. Similarly, some of the pigments that were applied, such as Prussian blue, and the binder correspond to technical developments in the 18th century, confirming once more their modern origin.

On the other hand, the Bāb Bayt al-Māl façade no longer contains any original mosaics as it has been completely restored in compliance with the Viollet-le-Duc's principle of “stylistic restoration”. The tesserae used in this mosaic have a completely different composition (high-lead glasses) with lead antimonate and calcium antimonate as inclusions to opacify the glass. These types of tesserae have not been identified in any other part of the mosaics, suggesting that the restorations remained confined to the Bāb Bayt al-Māl mosaic in line with contemporary newspaper reports.

The main changes in the Maqṣūrah mosaics and the characteristics of the tesserae used in each intervention are summarized in Table 3.

Table 3.

Summary of the main interventions and type of tesserae used in the Maqṣūrah of the Mosque-Cathedral of Córdoba.

  Data  Principal  Fact  Type of tesserae 
The Great Mosque of Córdoba  786–787  Abd al-Rahman I  Construction of the mosque   
  ∼840  Abd al-Rahman II  Expansion of the mosque   
  ∼960  Al-Hakam II  Expansion of the mosque and construction of the Miḥrāb and mosaics  Homogeneous coloured and gold-leaf soda-lime silicate and high-lead glasses 
  988  Almanzor  Expansion of the mosque   
The Mosque-Cathedral of Córdoba  1236  King Ferdinand III of Castile  Consecration of the Great Mosque of Córdoba to the Assumption of Mary   
  1390  –  Installation of the altarpiece of the Nursing Madonna in front of the Miḥrāb   
  1595  Antonio and Hernando Mohedano de Saavedra  Installation of the altarpiece “Última Cena” in front of the Bāb Bayt al-Māl chamber   
Modern interventions  1771–1772  Baltasar Dreveton  Restoration of the Miḥrāb dome   
  1815  Bishop Pedro Antonio de Trevilla  Dismounting the altarpiece of the Nursing Madonna from the Miḥrāb chamber   
  1817–1818  Mr. Patricio Furriel  Restoration of the mosaics of the Miḥrāb and Sābāṭ façades  Very pale high-alkaline glasses painted with blue, red, green or golden colours 
  1912  Ricardo Velázquez Bosco  Dismounting the altarpiece “Última Cena” from of the Bāb Bayt al-Māl chamber   
  1914–1916  J. & H. Maumejean Fréres  Reproduction and installation of the mosaic in the Bāb Bayt al-Māl chamber  Homogeneous coloured and gold-leaf high-lead glasses 
  1997–1999  Instituto Andaluz del Patrimonio Histórico (IAPH)  Consolidation of the mortars and reintegration of the tesserae   
Glossary

Hijri year (H): The era used in the Islamic lunar calendar.

Maqṣūrah: The ‘closed-off space’ near the centre of the Qiblah wall in the direction of prayer, usually

reserved for the caliph

Miḥrāb: Prayer niche in the Qiblah wall

Minbar: Wooden pulpit for the imam's sermon.

Muzŷŷaŷa: tesserae with glaze.

Qiblah: Wall of the mosque where the Mihrab opens, which is normally the direction towards the Sacred

Mosque in Mecca.

Qubba: Islamic domed shrine.

Conflict of interest

No potential conflict of interest was reported by the authors.

Acknowledgments

The authors acknowledge to Cabildo of Córdoba Cathedral, Instituto Andaluz del Patrimonio Histórico and the Research Unit VICARTE (FCT NOVA) for the facilities provided to accomplish this research, and to Biblioteca Nacional de España and Universitat Politècnica de Catalunya (UPCommons) for the permission of use of the images from their databases. This work was partially funded by the European Research Council under the European Union's Horizon 2020 research and innovation programme (grant agreement No. 647315 to NS) and the Fundación General CSIC (ComFuturo Programme). The authors wish to acknowledge the professional support of the Interdisciplinary Thematic Platform from CSIC Open Heritage: Research and Society (PTI-PAIS).

References
[1]
A. Villar Movellán.
La catedral de Córdoba.
Caja San Fernando, (2002),
[2]
R. Castejón.
Datos para la restauración de la Mezquita de Córdoba.
Arquitectura, 177 (1973), pp. 11-17
[3]
M.T. Casal García.
The Rabad of Saqunda in Umayyad Córdoba (750–818 AD).
Entre Civ. y Madina. El Mundo Las Ciudad. En La Península Ibérica y En El Norte África (Siglos IV–IX), pp. 119-132
[4]
M. Nieto Cumplido.
La Catedral de Córdoba, Publicaciones de la Obra Social y Cultural de Cajasur, Córdoba.
(1998),
[5]
M. Salcedo Hierro.
La Mezquita, Catedral de Córdoba: templo universal, cumbre de arte, vivero de historias y leyendas, Obra Social y Cultural de CajaSur, Córdoba.
(2000),
[6]
C. Abad Castro, I. González Cavero.
Una posible transformación del acceso a la maqsura de al-Hakam II en la mezquita de Córdoba durante el gobierno de al-Mansur.
Awraq, 17–18 (2018), pp. 229-250
[7]
G. Pizarro Berengena.
Los pasadizos elevados entre la mezquita y el Alcázar Omeya de Córdoba. Estudio arqueológico de los sābātāt.
Arch. Esp. Arqueol., 86 (2013), pp. 233-249
[8]
L. Torres Balbás.
Arte Hispanomusulmán. Hasta la caída del califato de Córdoba, in: España Musulmana Hast. La Caída Del Califato Córdoba (711–1031 d. J.C.), Espasa-Calpe, Madrid.
(1957), pp. 558-569
[9]
C. Abad Castro.
Nuevos datos acerca de la ampliación de al-Hakam II en la mezquita de Córdoba y algunas hipótesis sobre la zona de la maqsüra de época emiral.
Anu. Del Dep. Hist. y Teoría Del Arte., 25 (2013), pp. 9-22
[10]
Real Academia de San Fernando, Antigüedades Árabes de España, Imprenta Real, Madrid, 1804. http://bdh.bne.es/bnesearch/detalle/bdh0000229635.
[11]
M. Ocaña Jiménez.
Las inscripciones en mosaico del Mihrab de la Gran Mezquita de Córdoba y la incógnita de su data.
Les Mosaïques La Gd. Mosquée Cordoue,
[12]
J.M. Puerta Vílchez.
La monumentalidad y el sentido artístico de Qurtuba.
Awraq, 7 (2013), pp. 43-103
[13]
H. Stern.
Les mosaïques de la Grande Mosquée de Cordoue.
Walter de Gruyter, (1976),
[14]
E. Romero de Torres.
La famosa capilla del Mihrab, que amenazaba hundirse en la segunda mitad del siglo XVIII, fue restaurada por el arquitecto francés, don Baltasar Dreveton, D.
Córdoba, 30453 (1935), pp. 1
[15]
E. Romero de Torres.
Restauraciones desconocidas en la Mezquita-Aljama de Córdoba.
Boletín La Real Acad. Ciencias Bellas Let. y Nobles Artes Córdoba., 62 (1949), pp. 73-78
[16]
S. Herrero Romero.
Teoría y práctica de la restauración de la Mezquita-Catedral de Córdoba durante el siglo XX.
Universidad Politécnica de Madrid. Escuela Técnica Superior de Arquitectura, (2015),
[17]
M.A. Gómez-Morón, T. Palomar, L.C. Alves, P. Ortiz, M. Vilarigues, N. Schibille.
Christian-Muslim contacts across the Mediterranean: Byzantine glass mosaics in the Great Umayyad Mosque of Córdoba (Spain).
J. Archaeol. Sci., 129 (2021), pp. 105370
[18]
M.A. Gómez Morón.
Evaluación de la metodología mediante técnicas analíticas no invasivas para la investigación, caracterización y diagnóstico aplicada a casos del patrimonio cultural andaluz.
(2021),
[19]
J.A. Souto.
La Mezquita Aljama de Córdoba.
Artigrama Rev. Del Dep. Hist. Arte La Univ. Zaragoza, 22 (2007), pp. 37-72
[20]
M. Ocaña Jiménez.
Inscripciones árabes fundacionales de la mezquita-catedral de Córdoba.
Cuad. Madinat Al-Zahra Rev. Difusión Científica Del Conjunto Arqueol. Madinat Al-Zahra, 2 (1988), pp. 9-28
[21]
S. Calvo Capilla.
The visual construction of the Umayyad Caliphate in Al-Andalus through the Great Mosque of Cordoba.
Arts, 7 (2018), pp. 1-21
[22]
A. Alvarez Sotomayor.
Cartilla Geográfica de la Provincia de Córdoba, Imprenta de Santaló, Canalejas y Comp.
Cordoba, (1837),
[23]
R. Amador de los Ríos y Villalta.
Inscripciones árabes de Córdoba, Imprenta de Fortanet, Madrid.
(1879),
[24]
H. Ecker.
The Great Mosque of Córdoba in the twelfth and thirteenth centuries.
Muqarnas, 20 (2003), pp. 113-141
[25]
C. Abad Castro, I. González Cavero.
The royal chapel in the cathedral of cordoba. Some hypotheses on its royal patronage and construction process.
Anu. Estud. Mediev., 49 (2019), pp. 393-426
[26]
J. Valverde Madrid.
Datos para la historia de la pintura en Córdoba. II, El retablo del Adelantado Don Alfonso de Montemayor en la Catedral de Córdoba, Boletín La Real Acad. Ciencias.
Bellas Let. y Nobles Artes Córdoba, 78 (1958), pp. 123-142
[27]
Arte cristiano y belleza, El Políptico de la leche (2012). http://artecristianoybelleza.blogspot.com/2012/02/el-poliptico-de-la-leche.html.
[28]
J. Amador de los Ríos, R. Amador de los Ríos.
Villanta Litograph: Nave principal y Mihrab de la mezquita (Córdoba).
Monum. Arquit. España. Monum. Latino-Bizantinos Córdoba, (1879),
[29]
P. de Salazar, Gongora.
Planta de la Catedral (1741).
La Mezquita Córdoba Planos y Dibujos,
[30]
A. Ponz.
Planta de la Catedral de Córdoba (1791).
La Mezquita Córdoba Planos y Dibujos, Colegio Oficial de Arquitectos de Andalucia Occidental,
[31]
P. Navascués.
The protagonists of the “Antigüedades Árabes de España” and the san fernando royal academy of fine arts in Madrid.
Art Transl., 11 (2019), pp. 124-147
[32]
A. de Laborde.
Vista interior de la Iglesia Major de Cordova.
Voyag. Pittor. Hist. l’Espagne, 3 (1812), pp. 552
[33]
A. Gámiz-Gordo, A.J. García Ortega.
La primera colección de vistas de la Mezquita-Catedral de Córdoba en el Voyage de Laborde (1812).
Arch. Esp. Arte., 338 (2012), pp. 105-124
[34]
A. de Morales.
Las antiguedades de las ciudades de España, Casa de Juan Iñiguez de Lequeríca.
Alcala de Henares, (1575),
[35]
L.M. Ramirez, de las Casas-Deza.
Indicador cordobés, Imprenta de Don Rafael García, Córdoba.
(1837),
[36]
J. Brown.
La Edad de Oro de la pintura en España.
Editorial Nerea S.A, (1991),
[37]
P. Díaz Cayeros.
Pablo de Céspedes entre Italia y España.
An. Del Inst. Investig. Estéticas, 22 (2000), pp. 5-60
[38]
O. Hauser Muller, A. Menet Kurstiner.
Córdoba.
el Mirahb, (1891),
[39]
R. Garzón, Núm.
505 Córdoba. Galería y frente exterior del Mirab.
(1888),
[40]
Casa Moreno. Archivo de Arte Español (1893-1953), Córdoba- 44- La catedral [Mezquita]. Lateral de la capilla del Mihrab. Fototeca del Patrimonio Histórico, (n.d.). http://www.mcu.es/fototeca_patrimonio/Visor?usarVisorMCU=true&archivo=MORENO/preview/00872_C_P.jpg (accessed 8.9.20).
[41]
La Capilla de Villaviciosa en la Mezquita-Catedral de Córdoba (continuación), D. Córdoba. 9769 (1882) 8. https://prensahistorica.mcu.es/es/publicaciones/verNumero.do?idNumero=1000011100.
[42]
M. Lopez Dominguez, L.M. Aljama.
Breve ojeada sobre los descubrimientos últimos.
D. Córdoba, 14446 (1899), pp. 1
[43]
L. Torres Balbás.
La mezquita de Córdoba y las ruinas de Madinat Al-Zahra, Plus-Ultra, Madrid.
(1952),
[44]
R. Aguilar Priego.
Obras en la Torre de la Catedral de Córdoba desde el siglo XVII hasta nuestros días.
Boletín La Real Acad. Ciencias Bellas Let. y Nobles Artes Córdoba, 74 (1956), pp. 27-44
[45]
L. Torres Balbás.
Restauración en el siglo XVIII de la cúpula que precede al Mihrab de la Mezquita de Córdoba.
Al-Andalus, IV (1936), pp. 198-200
[46]
P. Marfil Ruiz.
Estudio de las linternas y el extradós de las cúpulas de la Maqsura de la Catedral de Córdoba, antigua mezquita Aljama.
Arqueol. La Arquit, 3 (2004), pp. 91-107
[47]
R. Aguilar Priego.
Datos inéditos sobre la restauración del mihrab de la Mezquita de Córdoba.
Boletín La Real Acad. Ciencias Bellas Let. y Nobles Artes Córdoba, 53 (1945), pp. 31-58
[48]
J. Caveda.
Memorias para la historia de la Real Academia de San Fernando, Imprenta de Manuel Tello, Madrid.
(1867),
[49]
S. Mora Alonso-Muñoyerro.
Restoration of monuments in Spain. Theory and practice.
Tech. Trans. Archit., 10 (2015), pp. 63-72
[50]
G. Ruiz Cabrero.
Dieciséis proyectos de Velázquez Bosco: la Mezquita-Catedral de Córdoba.
Rev. Nac. Arquit., 256 (1985), pp. 47-56
[51]
La sesión municipal de ayer, D. Córdoba. 20208 (1915) 1. https://prensahistorica.mcu.es/es/publicaciones/verNumero.do?idNumero=1000017270.
[53]
A. Bouzas Abad.
Estudio del estado de conservación de las cúpulas. Mezquita-Catedral de Córdoba, Instituto Andaluz del Patrimonio Histórico.
Consejería de Cultura, (2017),
[54]
A. Gomez-Moron, N. Schibille, L.C. Alves, A. Bouzas, P. Ortiz, M. Vilarigues, T. Palomar.
Characterization of glass tesserae from the Mosque of Cordoba (Spain).
Sci. Digit. Technol. Cult. Herit. – Interdiscip. Approach to Diagnosis, Vulnerability, Risk Assess. Graph. Inf. Model., pp. 258-262
[55]
I.C. Freestone.
Roman Glass.
Encycl. Glas. Sci. Technol., pp. 1261-1271 http://dx.doi.org/10.1002/9781118801017.ch10.3
[56]
K.H. Wedepohl, K. Gerth, K. Heide.
Experimental melts to explore the technique of medieval woodash glass production and the chlorine content of medieval glass types.
Chemie Der Erde, 58 (1998), pp. 219-232
[57]
C. Moretti, S. Hreglich.
Raw Materials, Recipes and Procedures Used for Glass Making, in: Modern Methods for Analysing Archaeological and Historical Glass.
John Wiley & Sons Ltd., (2013), pp. 23-47 http://dx.doi.org/10.1002/9781118314234.ch2
[58]
S. Cagno, M. Brondi Badano, F. Mathis, D. Strivay, K. Janssens.
Study of medieval glass fragments from Savona (Italy) and their relation with the glass produced in Altare.
J. Archaeol. Sci., 39 (2012), pp. 2191-2197
[59]
A. Smrcek.
Evolution of the compositions of commercial glasses 1830–1990. Part I. Flat glass.
Glas. Sci. Technol., 78 (2005), pp. 173-184
[60]
A. Smrcek.
Evolution of the compositions of commercial glasses 1830–1990. Part II. Container glass.
Glas. Sci. Technol., 78 (2005), pp. 230-244
[61]
J.J. Kunicki-Goldfinger, J. Kierzek, P. Dzierzanowski, A. Kasprzak.
Central European Crystal glass of the first half of the 18th century.
Ann Du 16th Congrès l’Association Int. Pour l’Histoire Du Verre, AIHV, (2005), pp. 258-262
[62]
M.L. Sempowski, A.W. Nohe, J.-F. Moreau, I. Kenyon, K. Karklins, S. Aufreiter, R.G.V. Hancock.
On the transition from tin-rich to antimony-rich european white soda-glass trade beads for the senecas of Northeastern North America.
J. Radioanal. Nucl. Chem., 244 (2000), pp. 559-566
[63]
E. Blair.
An XRF compositional analaysis of opaque white glass beads from 17th-century mission Santa Catalina de Guale, Georgia.
Beads J. Soc. Bead Res., 29 (2017), pp. 31-48
[64]
Institute of Chemistry University of Tartu, Database of ATR-FT-IR spectra of various materials (2022). https://spectra.chem.ut.ee/ (accessed 28.1.22).
[65]
P. Martín-Ramos, I.A. Fernández-Coppel, N.M. Ruíz-Potosme, J. Martín-Gil.
Potential of ATR-FTIR spectroscopy for the classification of natural resins.
Biol. Eng. Med. Sci. Rep., 4 (2018), pp. 3-6
[66]
R.J. Gettens, R.L. Feller, W.T. Chase.
Vermilion and Cinnabar.
Artist. Pigment. A Handb. Their Hist. Charact., Archetype Publications, pp. 159-182
[67]
R.J. Gettens, H. Kühn, W.T. Chase.
Lead white.
Artist. Pigment. A Handb. Their Hist. Charact., Archetype Publications, pp. 67-82
[68]
B.H. Berrie.
Prussian Blue.
Artist. Pigment. A Handb. Their Hist. Charact., pp. 191-218
[69]
C.R. Santos, M. Vilarigues, P. Dabas, I. Coutinho, T. Palomar.
Reproducing crystal glass from three 18–20th centuries Portuguese glass arcana.
Int. J. Appl. Glas. Sci., 11 (2020), pp. 743-755
[70]
M.J. González López.
La naturaleza de la capa de preparación según la visión de algunos de los principales tratadistas de la historia de la pintura.
Rev. PH., 19 (1997), pp. 57
[71]
L. De Viguerie, P.A. Payard, E. Portero, P. Walter, M. Cotte.
The drying of linseed oil investigated by Fourier transform infrared spectroscopy: historical recipes and influence of lead compounds.
Prog. Org. Coat., 93 (2016), pp. 46-60
[72]
F. Hernández Hernández.
La conservación del patrimonio histórico: Criterios internacionales.
El Patrim. Cult. La Mem. Recuper., Ediciones Trea, (2002), pp. 277-344
[73]
J.M. Fernández Navarro.
El vidrio. 3a ed Consejo Superior de Investigaciones Científicas.
Sociedad Española de Cerámica y Vidrio, (2003),
[74]
V. Gedzevičiute, N. Welter, U. Schüssler, C. Weiss.
Chemical composition and colouring agents of Roman mosaic and millefiori glass, studied by electron microprobe analysis and Raman microspectroscopy.
Archaeol. Anthropol. Sci., 1 (2009), pp. 15-29
[75]
H.X. Zhao, Q.H. Li, S. Liu, F.X. Gan.
Characterization of microcrystals in some ancient glass beads from China by means of confocal Raman microspectroscopy.
J. Raman Spectrosc., 44 (2013), pp. 643-649
[76]
P. Ricciardi, P. Colomban, A. Tournié, M. Macchiarola, N. Ayed.
A non-invasive study of Roman Age mosaic glass tesserae by means of Raman spectroscopy.
J. Archaeol. Sci., 36 (2009), pp. 2551-2559
[77]
V.S.F. Muralha, S. Canaveira, J. Mirão, S. Coentro, T. Morna, C.S. Salerno.
Baroque glass mosaics from the Capela de São João Baptista (Chapel of Saint John the Baptist, Lisbon): unveiling the glassmaking records.
J. Raman Spectrosc., 46 (2015), pp. 483-492
[78]
S. Yazdani Mehr.
Analysis of 19th and 20th century conservation key theories in relation to contemporary adaptive reuse of heritage buildings.
Heritage, 2 (2019), pp. 920-937
[79]
L. Torres Balbás.
La reparación de los monumentos antiguos en España.
Arquitectura, 15 (1933), pp. 1-10
Copyright © 2022. The Author(s)